Discoloration and mineralization of Reactive Red HE-3B by heterogeneous photo-Fenton reaction

Discoloration and mineralization of Reactive Red HE-3B were studied by using a laponite clay-based Fe nanocomposite (Fe-Lap-RD) as a heterogeneous catalyst in the presence of H2O2 and UV light. Our experimental results clearly indicate that Fe-Lap-RD mainly consists of Fe2O3 (meghemite) and Fe2Si4O10(OH)2 (iron silicate hydroxide) which have tetragonal and monoclinic structures, respectively, and has a high specific surface area (472m(2) / g) as well as a high total pore volume (0.547 cm(3)/g). It was observed that discoloration of HE-3B undergoes a much faster kinetics than mineralization of HE-3B. It was also found that initial HE-3B concentration, H2O2 concentration, UV light wavelength and power, and Fe-Lap-RD catalyst loading are the four main factors that can significantly influence the mineralization of HE-3B. At optimal conditions, complete discoloration of 100 mg/L HE-3B can be achieved in 30 min and the total organic carbon removal ratio can attain 76% in 120 min, illustrating that Fe-Lap-RD has a high photo-catalytic activity in the photo-assisted discoloration and mineralization of HE-3B in the presence of UV light (254nm) and H2O2. (C) 2003 Elsevier Science Ltd. All rights reserved.

A novel route to the synthesis of mesoporous Titania with full anatase nanocrystalline domains

A porous, high surface area TiO2 with anatase or rutile crystalline domains is advantageous for high efficiency photonic devices. Here, we report a new route to the synthesis of mesoporous titania with full anatase crystalline domains. This route involves the preparation of anatase nanocrystalline seed suspensions as the titania precursor and a block copolymer surfactant, Pluronic P123 as the template for the hydrothermal self-assembly process. A large pore (7 - 8 nm) mesoporous titania with a high surface area of 106 - 150 m(2)/g after calcination at 400degreesC for 4 h in air is achieved. Increasing the hydrothermal temperature decreases the surface area and creates larger pores. Characteristics of the seed precursors as well as the resultant mesoporous titania powder were studied using XRD analysis, N-2-adsorption/desorption analysis, and TEM. We believe these materials will be especially useful for photoelectrochemical solar cell and photocatalysis applications.